助催化剂对TiCl_4/MgCl_2催化丙烯高温聚合的影响

研究了助催化剂种类(三甲基铝、三异丁基铝、三正己基铝、三乙基铝和甲基铝氧烷)及其含量对无内、外给电子体的TiCl4/MgCl2催化剂催化丙烯高温(100℃)聚合性能的影响,并用结晶分级分析、示差扫描量热和凝胶渗透色谱等方法分析了所得聚丙烯的结晶熔融行为和微观结构。实验结果表明,聚合温度从70℃升至100℃时,TiCl4/MgCl2催化剂的定向能力基本不变;100℃聚合时,以烷基化能力较弱的三异丁基铝为助催化剂时TiCl4/MgCl2催化剂的活性最高,而采用烷基化能力最强的三甲基铝为助催化剂时TiCl4/MgCl2催化剂的活性最低;100℃聚合时,助催化剂的种类对TiCl4/MgCl2催化剂的定向能力影响很小。     

Oxidation of porous nanocrystalline titanium nitride. II. Scale structure and composition

We have used x-ray phase analysis to study the composition of the products of reaction between oxygen and nanocrystalline powders with particle sizes 15, 40, 55, and 80 nm, and also specimens pressed (and sintered) from them. The powders were oxidized in air at 100°C (400 h) to 500°C (5 min), while the sintered specimens were oxidized at 600–900°C for 15, 120, and 240 min. In all cases, in the initial oxidation step the oxynitride Ti(O_xN_y) is formed, which over time is oxidized to TiO, Ti₂O₃, Ti₃O₅, TiO₂ (anatase) and TiO₂ (rutile). In the range 600–800°C, formation of a continuous oxide layer and conversion of anatase to rutile slows down diffusion of oxygen in the scale. We have established that at 900°C, the growth rate of the scale thickness increases and so the reflections from the oxynitride are barely noticeable on the diffraction patterns taken from the surface of the oxidized specimen. In these diffraction patterns, along with strong reflections from the rutile, we also observed weak reflections from lower oxides and anatase, which may be due to reaction between oxygen and the titanium ions diffused to the scale surface. We have concluded that at T > 850°C, the mechanism for oxidation of TiN changes. This is due to superposition of counterdiffusion of titanium ions on the diffusion of oxygen. __________ Translated from Poroshkovaya Metallurgiya, Nos. 3–4(448), pp. 72–78, March–April, 2006.     

原位TiCp/Fe复合材料的切削力及切屑形状

从退火态原位TiCp／Fe复合材料的切削力和切屑形状方面分析了其切削性能。研究结果表明其切削力及切削力的波动范围都小于铸态45钢，其切削性能比45钢好。TiCp／Fe复合材料的切屑为C形屑、长紧卷屑和发条状卷屑，在机加工中，产生这几种切屑是比较理想的。从切屑方面看，TiCp／Fe复合材料的切削性能较好。     

复合聚全氟乙丙烯材料的介电及高频击穿性能研究

在聚全氟乙丙烯(FEP)中添加 TiO_2和 Al_2O_3,通过热压成型的方法制备了 FEP/TiO_2复合材料和 FEP/Al_2O_3复合材料,研究了氧化物添加量对复合材料介电常数、介电损耗和高频击穿性能的影响。结果表明,随氧化物含量的增加,复合材料的介电常数和介电损耗均增加;在同一添加量下,TiO_2对复合体系的介电性能影响较大。FEP/TiO_2复合材料的高频击穿性能随 TiO_2含量的增加而下降,在 TiO_2含量为4.0%(质量分数,下同)时,复合材料的损伤阈值已降为 FEP 材料损伤阈值的48.9 %。而 FEP/Al_2O_3复合材料的高频击穿性能随 Al_2O_3含量的增加而升高,当 Al_2O_3含量为1.2%时,复合材料的损伤阈值已增大到 FEP 材料损伤阈值的2倍,达到313 J/m~2。     

降低钛材价格、促进钛在舰船上的应用

舰船是武器装备和兵员在水上或水下的运动作战平台。空船质量很大。钛材是一种优秀的舰船结构材料，已广泛应用于潜艇壳体、机电设备中，但价格昂贵，用于空船质量的比例还很少，从设计质量分析中阐明，铁材降价1／3将有利于代替铜合金和不锈钢，在舰船上广泛推广。     

相转移法制备高纯超细TiO2技术研究

报道了用相转移法制备高纯超细ＴｉＯ２的新技术；探讨了Ｔｉ（Ⅳ）从有机相转移到水相发生水解反应的机理 ；通过ＴＧ－ＤＴＡ分析以及ＸＲＤ物相分析对水解产物的组成、热分解机理，晶型转变规律进行了研究，建立了水解产物焙烧的最佳温度。     

An investigation of pore cracking in titanium welds

Two welded Ti-6A1-4V pressure vessels leaked prematurely in service. The leaks were caused by cracks emanating from weld porosity. The cracks originated during fabrication, with subsequent growth in service leading to the formation of the leak paths. Pore cracking is thought to be caused by a mechanism that involves both sustained-load and cyclic contributions, with the former being the more prominent. It is shown that the tendency for cracking is influenced by pore position and that pore size is not a deciding factor in that regard. The factors that govern pore cracking are discussed, and the possible role of interstitial embrittlement is assessed.     

Superplastic behaviour of Ti-48at.%Al two-phase titanium aluminide compacts made from mechanically alloyed powder

An HIP compact of MA-processed powder having a nominal composition of Ti-48at.% Al was produced. The compact consisted of a large amount of TiAl(λ) and a small amount of Ti₃Al (₂), in a completely ultra-fine equiaxed grain structure. This two-phase compact showed typical superplastic deformation behaviour. A maximum elongation of 550% was obtained. A strain exponent, n = 2, and grain size exponent, p = 2, were determined from the results of a strain-rate-change test and a creep test at constant initial stress using samples having various grain sizes, respectively. The activation energy for creep, Q_c at constant stress was calculated to be 350 kJ/mole. It is concluded that the superplastic deformation mechanism of the material under study is grain boundary sliding controlled by lattice diffusion in the TiAl phase.     

钛对耐硫变换催化剂性能的影响

利用常压微反色谱、程序升温还原（ＴＰＲ）等技术研究了钛对耐硫变换催化剂性能的影响，结果表明：（１）钛能明显提高耐硫变换催化剂的活性，尤其是在低于６２３Ｋ时活性提高最为明显；（２）工业侧流试验后，含钛样品的保留活性及活性保留率均高于Ｋ８－１１；（３）催化剂中添加助剂ＴｉＯ２后，能显著提高对原料气中Ｈ２Ｓ含量变化的适应能力，因此可以拓宽对原料气的选择范围，对工业生产有着十分重要的现实意义。     

Formation of titanium and cobalt germanides on Si (100) using rapid thermal processing

Titanium and cobalt germanides have been formed on Si (100) substrates using rapid thermal processing. Germanium was deposited by rapid thermal chemical vapor deposition prior to metal evaporation. Solid phase reactions were then performed using rapid thermal annealing in either Ar or N₂ ambients. Germanide formation has been found to occur in a manner similar to the formation of corresponding silicides. The sheet resistance was found to be dependent on annealing ambient (Ar or N₂) for titanium germanide formation, but not for cobalt germanide formation. The resistivities of titanium and cobalt germanides were found to be 20 μΩ-cm and 35.3μΩ-cm, corresponding to TiGe₂ and Co₂Ge, respectively. During solid phase reactions of Ti with Ge, we have found that the Ti₆Ge₅ phase forms prior to TiGe₂. The TiGe₂ phase was found to form approximately at 800° C. Cobalt germanide formation was found to occur at relatively low temperatures (425° C); however, the stability of the material is poor at elevated temperatures.